低膨胀微晶玻璃
-
新闻发布时间：2012-12-12新闻浏览次数：2960新闻作者：锦泰特种玻璃
部分锂铝硅微晶玻璃的组成：单位：%（质量分数）
| SiO2 | Al2O3 | Li2O | MgO | ZnO | P2O5 | Na2O | K2O | BaO | TiO2 | ZrO2 | AS2O3 | 主晶相 |
| 68.8 | 19.2 | 2.7 | 1.8 | 1.0 | 0.2 | 0.1 | 0.8 | 1.8 | 2.7 | 0.8 | β-石英固溶体 | |
| 55.5 | 25.3 | 3.7 | 1.0 | 1.4 | 7.9 | 0.5 | 1.9 | 2.3 | 0.5 | β-石英固溶体 | ||
| 65.1 | 22.6 | 4.2 | 0.5 | 1.2 | 0.6 | 0.3 | 2.3 | 2.0 | 1.1 | β-石英固溶体 | ||
| 67.0 | 22.0 | 4.0 | 0.5 | 1.5 | 0.5 | 2.5 | 2.0 | β-石英固溶体 | ||||
| 69.05 | 18.9 | 3.3 | 0.9 | 1.55 | 0.2 | 0.1 | 0.75 | 1.75 | 2.6 | β-石英固溶体 | ||
| 65.7 | 22.0 | 4.5 | 0.5 | 1.1 | 0.5 | 0.3 | 2.0 | 2.5 | 1.0 | β-石英固溶体 | ||
| 66.7 | 20.5 | 3.5 | 1.6 | 1.2 | F0.22 | 4.8 | 0.05 | 0.4 | β-锂辉石固溶体 | |||
| 69.7 | 17.8 | 2.8 | 2.6 | 1.0 | 0.4 | 0.2 | 4.7 | 0.1 | 0.6 | β-锂辉石固溶体 |